Thermocouple Reference Tables Type B 1600 to 2140°F

Technical Reference | Temperature Related | Site Map | OMEGA Home Page

Thermocouple Reference Tables - Type B 1600 to 2140°F

Revised Thermocouple Reference Tables

TYPE B

NONE ESTABLISHED
Thermocouple Grade

Platinum-30% Rhodium
vs.
Platinum 6% Rhodium

Extension Grade

MAXIMUM TEMPERATURE RANGE
Thermocouple Grade
32 to 3092°F
0 to 1700°C
Extension Grade
32 to 212°F
0 to 100°C

LIMITS OF
ERROR
(whichever is Greater)
Standard: 0.5°C over 800°C
Special: NOT ESTABLISHED

COMMENTS, BARE WIRE ENVIRONMENT:
Oxidizing or Inert; Do Not Insert in Metal Tubes; Beware of Contamination; High Temperature; Common Use in Glass Industry

TEMPERATURE
IN DEGREES °C

REFERENCE JUNCTION
AT 0°C

░F	0	1	2	3	4	5	6	7	8	9	10	░F
Thermoelectric Voltage in mV

1600	3.717	3.722	3.726	3.731	3.735	3.740	3.744	3.749	3.753	3.758	3.763	1600
1610	3.763	3.767	3.772	3.776	3.781	3.786	3.790	3.795	3.799	3.804	3.809	1610
1620	3.809	3.813	3.818	3.822	3.827	3.832	3.836	3.841	3.845	3.850	3.855	1620
1630	3.855	3.859	3.864	3.869	3.873	3.878	3.882	3.887	3.892	3.896	3.901	1630
1640	3.901	3.906	3.910	3.915	3.920	3.924	3.929	3.934	3.938	3.943	3.948	1640

1650	3.948	3.952	3.957	3.962	3.966	3.971	3.976	3.980	3.985	3.990	3.994	1650
1660	3.994	3.999	4.004	4.009	4.013	4.018	4.023	4.027	4.032	4.037	4.041	1660
1670	4.041	4.046	4.051	4.056	4.060	4.065	4.070	4.075	4.079	4.084	4.089	1670
1680	4.089	4.093	4.098	4.103	4.108	4.112	4.117	4.122	4.127	4.131	4.136	1680
1690	4.136	4.141	4.146	4.151	4.155	4.160	4.165	4.170	4.174	4.179	4.184	1690


1700	4.184	4.189	4.194	4.198	4.203	4.208	4.213	4.217	4.222	4.227	4.232	1700
1710	4.232	4.237	4.242	4.246	4.251	4.256	4.261	4.266	4.270	4.275	4.280	1710
1720	4.280	4.285	4.290	4.295	4.299	4.304	4.309	4.314	4.319	4.324	4.328	1720
1730	4.328	4.333	4.338	4.343	4.348	4.353	4.358	4.362	4.367	4.372	4.377	1730
1740	4.377	4.382	4.387	4.392	4.397	4.401	4.406	4.411	4.416	4.421	4.426	1740

1750	4.426	4.431	4.436	4.441	4.445	4.450	4.455	4.460	4.465	4.470	4.475	1750
1760	4.475	4.480	4.485	4.490	4.495	4.500	4.504	4.509	4.514	4.519	4.524	1760
1770	4.524	4.529	4.534	4.539	4.544	4.549	4.554	4.559	4.564	4.569	4.574	1770
1780	4.574	4.579	4.584	4.589	4.593	4.598	4.603	4.608	4.613	4.618	4.623	1780
1790	4.623	4.628	4.633	4.638	4.643	4.648	4.653	4.658	4.663	4.668	4.673	1790


1800	4.673	4.678	4.683	4.688	4.693	4.698	4.703	4.708	4.713	4.718	4.723	1800
1810	4.723	4.728	4.733	4.738	4.743	4.748	4.754	4.759	4.764	4.769	4.774	1810
1820	4.774	4.779	4.784	4.789	4.794	4.799	4.804	4.809	4.814	4.819	4.824	1820
1830	4.824	4.829	4.834	4.839	4.844	4.850	4.855	4.860	4.865	4.870	4.875	1830
1840	4.875	4.880	4.885	4.890	4.895	4.900	4.905	4.911	4.916	4.921	4.926	1840

1850	4.926	4.931	4.936	4.941	4.946	4.951	4.957	4.962	4.967	4.972	4.977	1850
1860	4.977	4.982	4.987	4.992	4.998	5.003	5.008	5.013	5.018	5.023	5.028	1860
1870	5.028	5.034	5.039	5.044	5.049	5.054	5.059	5.065	5.070	5.075	5.080	1870
1880	5.080	5.085	5.090	5.096	5.101	5.106	5.111	5.116	5.121	5.127	5.132	1880
1890	5.132	5.137	5.142	5.147	5.153	5.158	5.163	5.168	5.173	5.179	5.184	1890


1900	5.184	5.189	5.194	5.199	5.205	5.210	5.215	5.220	5.225	5.231	5.236	1900
1910	5.236	5.241	5.246	5.252	5.257	5.262	5.267	5.273	5.278	5.283	5.288	1910
1920	5.288	5.294	5.299	5.304	5.309	5.315	5.320	5.325	5.330	5.336	5.341	1920
1930	5.341	5.346	5.351	5.357	5.362	5.367	5.373	5.378	5.383	5.388	5.394	1930
1940	5.394	5.399	5.404	5.410	5.415	5.420	5.425	5.431	5.436	5.441	5.447	1940

1950	5.447	5.452	5.457	5.463	5.468	5.473	5.479	5.484	5.489	5.495	5.500	1950
1960	5.500	5.505	5.511	5.516	5.521	5.527	5.532	5.537	5.543	5.548	5.553	1960
1970	5.553	5.559	5.564	5.569	5.575	5.580	5.585	5.591	5.596	5.601	5.607	1970
1980	5.607	5.612	5.618	5.623	5.628	5.634	5.639	5.644	5.650	5.655	5.661	1980
1990	5.661	5.666	5.671	5.677	5.682	5.688	5.693	5.698	5.704	5.709	5.715	1990


2000	5.715	5.720	5.725	5.731	5.736	5.742	5.747	5.752	5.758	5.763	5.769	2000
2010	5.769	5.774	5.780	5.785	5.790	5.796	5.801	5.807	5.812	5.818	5.823	2010
2020	5.823	5.828	5.834	5.839	5.845	5.850	5.856	5.861	5.867	5.872	5.878	2020
2030	5.878	5.883	5.888	5.894	5.899	5.905	5.910	5.916	5.921	5.927	5.932	2030
2040	5.932	5.938	5.943	5.949	5.954	5.960	5.965	5.971	5.976	5.982	5.987	2040

2050	5.987	5.993	5.998	6.004	6.009	6.015	6.020	6.026	6.031	6.037	6.042	2050
2060	6.042	6.048	6.053	6.059	6.064	6.070	6.075	6.081	6.086	6.092	6.098	2060
2070	6.098	6.103	6.109	6.114	6.120	6.125	6.131	6.136	6.142	6.147	6.153	2070
2080	6.153	6.159	6.164	6.170	6.175	6.181	6.186	6.192	6.197	6.203	6.209	2080
2090	6.209	6.214	6.220	6.225	6.231	6.237	6.242	6.248	6.253	6.259	6.264	2090


2100	6.264	6.270	6.276	6.281	6.287	6.292	6.298	6.304	6.309	6.315	6.320	2100
2110	6.320	6.326	6.332	6.337	6.343	6.349	6.354	6.360	6.365	6.371	6.377	2110
2120	6.377	6.382	6.388	6.394	6.399	6.405	6.410	6.416	6.422	6.427	6.433	2120
2130	6.433	6.439	6.444	6.450	6.456	6.461	6.467	6.473	6.478	6.484	6.490	2130
2140	6.490	6.495	6.501	6.507	6.512	6.518	6.524	6.529	6.535	6.541	6.546	2140

░F	0	1	2	3	4	5	6	7	8	9	10	░F

Thermocouple Reference Tables | Temperature Related Articles | Technical Reference | Site Map | Home

Please E-Mail your comments to OMEGA.COM™
or call us @1.800.TC-OMEGA^SM

Revised Thermocouple Reference Tables TYPE B

Platinum-30% Rhodium vs. Platinum 6% Rhodium

Revised Thermocouple Reference Tables

TYPE B

Platinum-30% Rhodium
vs.
Platinum 6% Rhodium